Model number： HT-02

    HT – High-Translucency Monochromatic Colored Zirconia (Made to Order)

    Product Description

    Structural Design:
    3Y composition with 41% translucency — combining strength with a natural appearance.

    The HT Series is a single-shade, pre-shaded 3Y zirconia that offers 1400 MPa flexural strength and 41% translucency, striking a balance between aesthetics and functionality.
    Compared to the LT series, it delivers a more natural light diffusion, making it ideal for restorations where both beauty and performance matter.
    It is also suitable for medium-span bridges and full-arch restorations, offering a stable yet visually pleasing solution.

    Indications:
    Single crowns, short to medium-span bridges, functional anterior restorations, full-arch fixed prostheses

    Key Features:
    Soft, natural shade expression — ideal for daily restorative cases and clinical designs requiring enhanced aesthetics

    Raw Material Distribution

    Translucency: 41%
    Sizes: 98mm × 12, 14, 16, 18, 20, 25, 30 mm (12mm and 30mm are made to order)
    Flexural Strength: 1400 MPa
    Available Shades: A2, A3, A3.5

    Indications

    Full-arch

    Sintering Curve

    Up to 3 Units (8 Hours Total)
    • Heat at 10°C/min to 900°C, hold for 20 minutes
    • Continue heating at 5°C/min to 1500°C, hold for 120 minutes
    • Cool down at 10°C/min to 300°C
    HT – High-Translucency Monochromatic Colored Zirconia (Made to Order)
    4–6 Unit Bridge (11.5 Hours Total)
    • Heat at 5°C/min to 900°C, hold for 30 minutes
    • Continue heating at 3°C/min to 1500°C, hold for 120 minutes
    • Cool down at 8°C/min to 300°C
    HT – High-Translucency Monochromatic Colored Zirconia (Made to Order)
    7+ Unit Bridge (16.4 Hours Total)
    • Heat at 5°C/min to 900°C, hold for 20 minutes
    • Continue heating at 2°C/min to 1500°C, hold for 120 minutes
    • Cool down at 3°C/min to 900°C
    • Then cool down at 7°C/min to 200°C
    HT – High-Translucency Monochromatic Colored Zirconia (Made to Order)