Model number： SHT-CML

    SHT-CML – Ultra-Translucent Multilayer Zirconia

    Product Description

    Structural Design:
    Single-structure 5Y-TZP, full-layer color gradient
    The SHT-CML series is made from stable 5 mol% yttria-stabilized zirconia (5Y-TZP), offering a balance of high translucency (~47%) and flexural strength (~900 MPa).
    It is specifically designed for daily restorative cases where both esthetics and durability are required.

    Featuring a natural multilayer shade gradient and smooth color transitions, SHT-CML delivers lifelike appearance without veneering porcelain.
    It is suitable for anterior and posterior single crowns, short to medium-span bridges, and any case where both appearance and structural reliability are essential.

    Indications:
    Anterior/posterior single crowns, short to medium-span bridges, daily restorative applications

    Key Features:
    • Single 5Y-TZP structure for optimized strength and translucency
    • Natural color gradient for a vivid, lifelike look without porcelain layering
    • Reliable performance and esthetic appeal in one material
    • Ideal for esthetic-focused yet clinically durable restorations

    Raw Material Distribution

    Translucency: 47%
    Sizes: 98mm × 12, 14, 16, 18, 20, 25, 30 mm (12mm and 30mm are made to order)
    Flexural Strength: 900 MPa
    Available Shades:A1, A2, A3, A3.5, A4, B1, B2, B3

    Indications

    Anterior and posterior restorations, up to 1–6 units

    Sintering Curve

    Up to 3 Units (8 hours total)
    • Heat at 10°C/min to 900°C, hold for 20 minutes
    • Continue heating at 5°C/min to 1500°C, hold for 120 minutes
    • Cool down at 10°C/min to 300°C
    SHT-CML – Ultra-Translucent Multilayer Zirconia
    4–6 Unit Bridge (11.5 hours total)
    • Heat at 5°C/min to 900°C, hold for 30 minutes
    • Continue heating at 3°C/min to 1500°C, hold for 120 minutes
    • Cool down at 8°C/min to 300°C
    SHT-CML – Ultra-Translucent Multilayer Zirconia
    7+ Unit Bridge (16.4 hours total)
    • Heat at 5°C/min to 900°C, hold for 20 minutes
    • Continue heating at 2°C/min to 1500°C, hold for 120 minutes
    • Cool down at 3°C/min to 900°C
    • Then cool down at 7°C/min to 200°C
    SHT-CML – Ultra-Translucent Multilayer Zirconia