    SHT – High-Strength Monochromatic Colored Zirconia

    Product Description

    Structural Design:
    Built with a 5Y-stabilized structure, the SHT series offers a flexural strength of approximately 900 MPa, making it ideal for restorations under high occlusal load, such as long-span bridges and full-arch fixed prostheses.

    Product Features:
    This single-shade colored zirconia delivers stable coloration, supports custom staining, and is compatible with liquid ceramic systems for individualized aesthetic adjustments.
    Combining high strength with clinical esthetics, it enhances restoration durability and visual quality.

    Indications:
    Long-span bridges, full-arch fixed prostheses, restorations requiring high structural strength

    Key Features:Outstanding strength and structural stability、Ideal for high-load occlusal restorations、Allows for custom staining and flexible adaptation to various clinical situations、Monochromatic design paired with a stable shade system for both esthetics and function
     

    Raw Material Distribution

    Translucency: 47%
    Sizes: 98mm × 12, 14, 16, 18, 20, 25, 30 mm (12mm and 30mm are made to order)
    Flexural Strength: 900 MPa
    Available Shades:
    A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4
     

    Indications

    1–6 units

    Sintering Curve

    Up to 3 Units (8 hours total)
    • Heat at 10°C/min to 900°C, hold for 20 minutes
    • Continue heating at 5°C/min to 1500°C, hold for 120 minutes
    • Cool down at 10°C/min to 300°C
    SHT – High-Strength Monochromatic Colored Zirconia
    4–6 Unit Bridge (11.5 hours total)
    • Heat at 5°C/min to 900°C, hold for 30 minutes
    • Continue heating at 3°C/min to 1500°C, hold for 120 minutes
    • Cool down at 8°C/min to 300°C
    SHT – High-Strength Monochromatic Colored Zirconia
    7+ Unit Bridge (16.4 hours total)
    • Heat at 5°C/min to 900°C, hold for 20 minutes
    • Continue heating at 2°C/min to 1500°C, hold for 120 minutes
    • Cool down at 3°C/min to 900°C
    • Then cool down at 7°C/min to 200°C